KAJI EKSPERIMEN UMUR LELAH POROS PADA AL 6061-ABU BATUBARA YANG MENDAPAT PERLAKUAN PANAS

Zainun Achmad, Hendrawan Harry Prasetya

Abstract


Fatigue is one of the main causes of failure contruction. Usually material fatigue fracture occurs in poros.
Poros a machine element that serves to connect from one machine element to other element . A shaft having a
different material composition-this different.research has the objective to study the fatigue life of a shaft with a
material 6061-coal bottom ash results that occur in the home foundry industry after heat treatment t6 and there
were no treatment is done, the results of the specimens to be tested weariness.
The method used to determine the fatigue life of a material shaft 6061-ash coal rotary bending fatigue test
according to standard JIS Z2274 with weights 0.7 σu and 0.9 σu of tensile strenght obtained from tensile test.
The results of fatigue testing and calculation methods of statistical probability of 10 % , 50 % and 90% of materials
that are subjected to heat for 2 hours with a load of 0.9 σu with a probability of 90 % that has the shorte st fatigue
life and fatigue life is highest specimens without heat treatment with a load of 0.7 σu with a probability of 10 % .
This percentage has increased 2x specimen lelah.Jadi age even make the heat treatment cycle of the material to be
low.

Keyword : Fatigue life ,Alumunium,Heat treatment


References


M.Dafid A. 201. Analisa Pengaruh Temperatatur

dan Waktu Aging T6 Terhadap Sifat Mekanik DISC

Brake Komposit Al-Abu Dasar Batubara Dari Hasil

Metode HAS

Jangkung Tri Pamungkas.2006. Optimasi umur lelah

plat komposit Al6061-abu batubara perlakuan

thermomekanis T8

Slamet Riyanto. 2006. Analisa Kelelahan Komposit

Al 6061-Abu Batu Bara

ITS-Master-18216-4108203002-Presentation-1-2

Uji Kelelahan

Abrianto Akuan ST. MT Diktat Kuliah Kelelahan

Logam Universitas Jenderal Ahmad Yani

Hendri Chandra. Fatigue Life Prediction Teknik

Mesin Universitas Sriwijaya

Handbook Alumunium

Handbook material of metalurgi


Refbacks

  • There are currently no refbacks.