Analisa Pengaruh Proteksi Anoda Aluminium terhadap Luasan Korosi pada Pelat Baja Karbon Rendah menggunakan Media Air Laut
Abstract
Corrosion rate analysis on the surface of commercial steel dan aluminum materials in agitation seawater media. Corrosion is a decrease in metal quality caused by the environment or chemicals and affects the condition material, as well as commercial steel. Several factors that influence the corrosion rate include salinity, pH, temperature and oxygen solubility in the corrosion medium. To calculate the corrosion rate of commercial steel and aluminum in seawater media can be used the weight lost method and the electrochemical method. This study uses the method of weight loss, and for corrosion media used seawater tide conditions and low tide conditions by adding pumps to circulate oxygen in the corrosion medium. From the results of the study it was found that the weight reduction in low tide conditions was greater than the tide conditions which affected the corrosion rate.
Keywords: Corrosion, Commercial Steel, Aluminum, weight lost method, sea water.
Korosi merupakan penurunan mutu logam yang diakibatkan oleh lingkungan atau zatkimia dan berpengaruh pada kondisi material, demikian halnya pada baja komersil. Beberapa faktor yang berpengaruh terhadap laju korosi diantaranya salinitas, pH, temperature dan kelarutan oksigen dalam media korosi. Untuk menghitung laju korosi baja komersil dan aluminium dalam media air laut dapat digunakan metode kehilangan berat (weight lost) dan metode elektrokimia. Penelitian ini menggunakan metode kehilangan berat, dan untuk media korosidigunakan air laut kondisi pasang dan kondisi surut dengan penambahan pompa untuk mensirkulasi oksigen dalam media korosi. Dari hasil penelitian diperoleh bahwa pengurangan berat pada kondisi surut lebih besar dibandingkan kondisi pasang yang berpengaruh pada laju korosi.
Kata Kunci: Korosi, Baja komersil, Aluminium, Metode kehilangan berat (weight lost), air laut.
Downloads
References
Denny A.J. 1997, “principles and Prevention of Corrosion, 2ed”.Singapore : Prentice Hall Internasional, Inc.
Fontana, M.G. 1994, “Corrosion Engineering”. New York : McGrawHikllbook company.
Musnasir. 2009, “laju korosi baja SC 42 dalam media air laut dengan metode immers total”, Seminar Nasional Penelitian, pendidikan dan penerapan MIPA, Universitas negeri Yogyakarta.
Saputra R. 2011, “Studi pengaruh ekstrak daun the rosella (hibiscuss abdariffa) sebagai green corrosion inhibitor untuk material baja karbon rendah di lingkungan NaCl 35% pada temperature 40*C “ , skripsi, fakultas teknik Departemen Metalurgi dan material, ITB.
Suardi, I.K. , dan Suarsana., 2007, “Prediksi laju korosi dengan perubahan besar derajad deformasi plastis dan media pengkorosi pada material baja karcon” , jurnal ilmiah teknik mesin cakram vol. 1 No.1.
Widharto S. 1999, “karan dan pencegahan” , PT. Pradnya Paramita, Jakarta.
Trethewey K.R. & chamberlain J. 1991, korosi untuk mahasiswa sains dan rekayasa, PT Gramedia Pustaka Utama, Jakarta.
Mekanika : Jurnal Teknik Mesin allows readers to read, download, copy, distribute, print, search, or link to the full texts of its articles and allow readers to use them for any other lawful purpose. The journal allows the author(s) to hold the copyright without restrictions. Finally, the journal allows the author(s) to retain publishing rights without restrictions